超滤膜处理地表水的试验研究
李建华1，郑敏聪1，赵晶2
安徽省电力科学研究院（合肥 230022）；
2.安徽华电宿州发电有限公司（宿州 234101）
[摘 要] 通过中试，研究了PVDF 材质的超滤膜处理地表水的效果及其工艺性能。试验结果表明：在试验过程中，该超滤膜的自用水率为7.82%，膜TMP 变化在0.03MPa 左右，膜产水浊度小于0.15NTU，膜产水SDI15 在2~3 之间，膜对化学耗氧量的去除率为18.18～24.35%，各项指标均达到DL/Z 952-2005《火力发电厂超滤水处理装置验收导则》要求和反渗透设备进水水质要求。
[关键词] 超滤 地表水 自用水率 跨膜压差 SDI
Pilot Test on Ultrafiltration of Surface Water
Li Jianhua1, Zhengmingchong1, Zhao Jing2
1.Anhui Electric Power Research Institute, Hefei 230022
2.Anhui CHD Suzhou Power Generation Co., LTD., Suzhou 234101
Abstract: It had been investigated that the effect and performance of the PVDF ultrafiltrationmembrane for
treating the surface water. The experimental results indicated that the auxiliary water ratio of themembrane was
7.82%, TMP was less than 0.03MPa, turbidity of the permeate was less than 0.15NTU, SDI15 was between 2 to 3,
the removal rate of COD was between 18.18% to 24.35%, which were allmet with DL/Z 952-2005《Guide for the
Acceptance of Ultrafiltration Equipment for Water Treatment in Fossil Fuel Power Plant》and the inlet water quality
need of the RO. So themembrane could be used for the pretreatment of the surface water RO.
Keywords: Ultrafiltration Surface Water Auxiliary water ratio TMP SDI
某超临界火力发电机组锅炉补给水系统设计水源为安徽宿州新汴河河水，拟采用超滤作为反渗透装置进水的预处理设备。由于目前市面上超滤膜种类繁多，超滤设备的运行和反洗工艺各不相同，电厂拟通过中型试验进行超滤设备的选型工作。针对新汴河的水质特点，通过合理的试验选择合适的膜组件、膜通量以及运行方式。
1 试验条件
1.1 试验工艺流程
试验在新汴河附近进行，试验用水为新汴河水，经混凝（聚合氯化铝）、杀菌（NaClO）处理的新汴河水经过砂滤处理后，进入超滤装置。试验工艺流程如图1 所示。

1.3 自用水率
由于超滤设备运行时，超滤膜的反洗、正洗等过程的用水均需要用到超滤产水，因此，在设计超滤膜组件和对超滤设备的经济运行状况等指标进行考核时，需考虑超滤设备的自用水率。
在本次中试试验过程中，超滤膜组件的自用水率计算如下：

2 结果与分析
2.1 膜进出水pH、电导率分析
试验过程中对总进水和超滤膜进出水的pH、电导率均进行了测量。pH 在7.6～7.9 之间，电导率750～1000μs/cm 之间。
2.2 膜进/出水压力和TMP（跨膜压差）分析